Ultimate tensile strength of total and self-etch adhesives: Effect of light irradiation distance.

  • Maan M. Nayif Department of Conser-vative Dentistry, College of Dentistry, Mosul University, Mosul, Iraq.


Objective: To evaluate the ultimate tensile strength (UTS) of total and self- etch adhesives irradiated at different distances. Materials and Methods: Sixty cylindrical specimens of 0.78mm diameter and 10 mm length were prepared of two types of adhesive systems total etch Excite DSC (EX – Ivoclar Vivadent, Schaan, Liechtenstein) and one-step self-etch Clearfil S3 Bond (S3, Kuraray Medical Inc., Tokyo, Japan). Specimens of each adhesive were divided into three groups according to the light irradiation distance (0, 2, 4mm) (n=10). Each specimen was attached to universal testing machine (Digital Force Gauge, IMADA CO., LTD, Japan) and loaded at cross head speed of 1mm/min until failure. Data were analyzed using two-way ANOVA and Independent Student t-test at p< 0.05. Results: Mean UTS for total etch (24.63, 18.19, 17.26 Mpa) and for self-etch (12.68, 8.53, 7.58Mpa) at (0, 2, 4mm) distances. Specimens irradiated directly show significantly the highest UTS while those irradiated at 4mm show the lowest values (p<0.05). Excite DSC total etch adhesive have higher UTS than Clearfil S3 self-etch adhesive regardless of irradiation distance (p<0.05).Conclusions: The UTS of the evaluated adhesives was light irradiation distance and adhesive system dependant.


1. Ilie N, Stark K. Effect of different curing protocols on the mechanical properties of low-viscosity bulk-fill composites. Clin Oral Investig. 2015; 19(2):271-9.
2. Araújo-Neto VG, Nobre CFA, De Paula DM, Souza LC, Silva JC, Moreira MM, Picanço PRB, Feitosa VP. Glycerol-dimethacrylate as alternative hydrophilic monomer for HEMA replacement in simplified adhesives. J Mech Behav Biomed Mater. 2018;1(82):95-101.
3. Hosaka K, Nakajima M, Takahashi M, Itoh S, Ikeda M,Tagami J, et al. Relationship between mechanical properties of one-step self-etch adhesives and water sorption. Dent Mater. 2010; 26 (4):360–7.
4. Denis AB, Diagone CA, Plepis AM, Viana RB. The effect of the polymerization initiator and light source on the elution of residual Bis-GMA and TEGDMA monomers: A study using liquid chromatography with UV detection. Spectrochim Acta Mol Biomol Spectrosc. 2015; 5 (151): 908-915.
5. Rullman I, Patyna M, Janssen B, Willershausen B. Determination of polymerization shrinkage of different composites using a photoelastic method. Am J Dent. 2017;30(1):16-22.
6. Filho JD, Poskus LT, Guimarães JGA, Barcellos AA, Silva EM. Degree of conversion and plasticization of dimethacrylate based polymeric matrices: influence of light-curing mode. J Oral Sci. 2008; 50(3): 315-321.
7. Maleknejad F, Ameri H, Manafi S, Chasteen J, Ghavamnasiri M. The effect of photoactivation time and light tip distance on the degree of conversion of light and dual-cured dentin adhesives. Indian J Dent Res. 2013; 24(2):225-8.
8. Sakano W, Nakajima M, Prasansuttiporn T, Foxton R and Tagami J. Polymerization behavior within adhesive layer of one- and two-step self-etch adhesives: A micro-Raman spectroscopic study. Dent Mater J. 2013; 32(6): 992–8.
9. Navarra CO, Cadenaro M, Frassetto A, Fontanive L, Di Lenarda R, Breschi L. Degree of Conversion of Self-etch Adhesives: In Situ Micro-Raman Analysis. Oper Dent. 2016; 41(5):501-510.
10. Pucci CR, Gu LS, Zeng C, Gou YP, Tay FR, Niu LN. Susceptibility of contemporary single-bottle self-etch dentine adhesives to intrinsic water permeation. J Dent. 2017;66:52-61.
How to Cite
NAYIF, Maan M.. Ultimate tensile strength of total and self-etch adhesives: Effect of light irradiation distance.. Journal of Oral Research, [S.l.], p. 44-47, aug. 2019. ISSN 0719-2479. Available at: <https://joralres.com/index.php/JOR/article/view/joralres.2019.091>. Date accessed: 16 oct. 2021. doi: https://doi.org/10.17126/joralres.2019.091.